# Optical constants for Ni2Al3 created by PTB # Reconstructed from reflection measurements in the wavelength range 10 - 16 nm # 30 nm Ni2Al3 thin film on 30 nm SiO on Si (measured 04/2016) # n = (1-delta) - (i*beta) # # lambda/nm 1-delta beta # ------------------------ 10.00 0.98527 0.03044 10.10 0.98532 0.03158 10.20 0.98547 0.03202 10.30 0.98554 0.03266 10.40 0.98574 0.03349 10.50 0.98626 0.03453 10.60 0.98687 0.03463 10.70 0.98712 0.03486 10.80 0.98751 0.03509 10.90 0.98778 0.03514 11.00 0.98783 0.03544 11.10 0.98792 0.03569 11.20 0.98793 0.03610 11.30 0.98781 0.03686 11.40 0.98902 0.03709 11.50 0.98920 0.03660 11.60 0.98795 0.03715 11.70 0.98823 0.03765 11.80 0.98755 0.03849 11.90 0.98746 0.03929 12.00 0.98711 0.04009 12.10 0.98683 0.04093 12.20 0.98706 0.04164 12.30 0.98777 0.04278 12.40 0.98846 0.04329 12.50 0.98900 0.04375 12.60 0.98942 0.04461 12.70 0.98967 0.04597 12.80 0.99018 0.04681 12.90 0.99080 0.04759 13.00 0.99143 0.04799 13.10 0.99194 0.04837 13.20 0.99247 0.04869 13.30 0.99311 0.04903 13.40 0.99362 0.04929 13.50 0.99424 0.04923 13.60 0.99489 0.04918 13.70 0.99539 0.04891 13.80 0.99591 0.04862 13.90 0.99642 0.04836 14.00 0.99682 0.04805 14.10 0.99733 0.04789 14.20 0.99743 0.04784 14.30 0.99762 0.04777 14.40 0.99786 0.04756 14.50 0.99793 0.04741 14.60 0.99799 0.04701 14.70 0.99839 0.04679 14.80 0.99810 0.04639 14.90 0.99800 0.04617 15.00 0.99788 0.04568 15.10 0.99746 0.04514 15.20 0.99688 0.04463 15.30 0.99639 0.04452 15.40 0.99595 0.04489 15.50 0.99604 0.04574 15.60 0.99590 0.04605 15.70 0.99570 0.04593 15.80 0.99564 0.04625 15.90 0.99560 0.04668 16.00 0.99542 0.04668